PET Filament Nonwoven Geotextile
Polyester nonwoven filament geotextile made from virgin PET(polyester) chips, the continuous filament was extruded from PET chip by machine directly by spun bound process, and then punch together to get the stable 3D with higher strength fabric. So, it has high strength, good creep property excellent and erosion resistance aging-resistance, filtration, reinforcement and heat resistance.
Specification:
(1). 80g/m2~1000g/m2
(2). 1m~8m in roll width, the length as client's request.
(3). Color: white , black , green or at your request
Property:
(1). Good flexibility, resistant to corrosion, resistant to acids and alkali, anti-oxidation
(2). Separation, filtration, drainage, reinforcement , protection and maintentance function.
Shandong Jinruixiang geotextile material Co.,Ltd
Shandong Famous Brand
Certificate of Inspection of Quality:CRCC Certification
Enterprise of Abiding by Strictly Contract and Being Trustworthy
ISO9001:2008 Quality Management System Certification; National Industrial Production License.
1.Water conservancy project and hydropower projects
2.Road paving, railway
3.Airport and port
4.River band protection and tunnel
5. Environmental protectiom, etc
Packaging Details:
Nonwoven Geotextile is packed in the woven bags or follow your demand.
Keep it away from moisture and fire!!!
Delivery Detail:
Generally within 5-15 days after receipt 30%T/T deposit !
Long Fiber Geotextile,Polyester Geotextile Fabric,Polyester Nonwoven Geotextile,Elcoseal Geosynthetic Clay Liner Shandong Jinruixiang Geotextile Material Co., Ltd , https://www.jrxgeosynthetics.com
1. Main features (1) Compared with general circular blade cutters, the feed rate is increased by about 3 times, the speed is increased by about 1 time, the processing efficiency is increased by more than 6 times, and the tool life is more than 3 hours.
(2) The strength, toughness and chipping resistance of the new TiAIN coated inserts are improved.
(3) The unique cutter body design improves the strength of the cutter body and the chip discharge performance is good.
2. Processing example: A mold manufacturer in Italy uses the milling cutter to process the mold. The machine is a FAMUT700 (15kW) machine tool, and the machined parts are plastic molds. The parts are ORVAL2344.135kg/mm2, equivalent to 4Cr5MoSiV, and the hardness is HRC40~41. For the company's DDM2160-80W20 mold milling cutter, the cutter size is φ16 straight shank type, the insert type is RDHX1003MO, and the insert type is JC5040 (TiALN coated insert).
3. Cutting conditions Speed: 2300rpm
Feed: 2500mm/min
Cutting width af: 1.5mm
Cutting depth pf: 0.5mm
Cutting method: spiral reaming Cooling method: wet (emulsion)
Gram weight
Thickness(mm)
Breaking strength(kn/m)
CBR burst strength(KN)
Elongation at break(%
Tear Strength(KN)
Sieve size O99(O35)mm
100
0.9
2.5
0.3
25-100
0.08
0.07-2.0
150
1.3
4.5
0.6
25-100
0.12
0.07-2.0
200
1.7
6.5
0.9
25-100
0.16
0.07-2.0
250
2.1
8
1.2
25-100
0.2
0.07-2.0
300
2.4
9.5
1.5
25-100
0.24
0.07-2.0
350
2.7
11
1.8
25-100
0.28
0.07-2.0
400
3
12.5
2.1
25-100
0.33
0.07-2.0
450
3.3
14
2.4
25-100
0.38
0.07-2.0
500
3.6
16
2.7
25-100
0.42
0.07-2.0
600
4.1
19
3.2
25-100
0.46
0.07-2.0
800
5
25
4
25-100
0.6
0.07-2.0
Japan Jiejie company DIEMATE high efficiency mold milling cutter
The DIEMATE series of mold milling cutters is a new high-efficiency and high-stability cutting tool developed by DIJET for mold processing requirements in home appliances and automobile manufacturing. This type of tool has a complete structure, including a milling cutter (edge ​​diameter 50mm ~ 160mm) widely used for milling, NC, CNC milling and copy milling, and a clip-on end mill for die cavity milling and engraving milling (blade diameter) 12mm, 15mm, 20mm).
Technical data sheet of polypropylene geotextile
Technical data sheet of polyester geotextile
Company Information
Product Equipment
Customer feedback
Why choose us
Product Application
Packaging & Shipping
FAQ